عنوان انگلیسی INVESTIGATING THE fFORMATION OF INTERMETALLIC COMPOUNDS AND THE VARIATION OF BOND STRENGTH BETWEEN Al-Cu LAYERS AFTER ANNEALING IN PRESENCE OF NICKEL BETWEEN LAYERS
چکیده انگلیسی مقاله In the present study, the effect of post-rolling annealing heat treatment on the formation of intermetallic compounds between Al-Cu strips, in the presence of nickel coating on the Cu strips, was investigated. In addition, the effect of post-rolling annealing and intermetallic compounds on the bond strength of Al-Cu strips was evaluated. In order to prepare samples, Cu strips were coated with nickel by electroplating process. After surface preparing, Cu strips were placed between two Al strips and roll bonded. This method is used for producing Al-Ni-Cu composites. Then the samples were annealed at 773K for 2 h. The formation of intermetallic compounds was studied using energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). Also, in order to investigate bond strength of Al-Cu after post-rolling annealing heat treatment, samples were produced using nickel powder and nickel coating. Then bond strength of strips was investigated using peeling test. The results revealed that by post-rolling annealing of layers, the bond strength between Al-Cu strips decreases dramatically.
کلیدواژه‌های انگلیسی مقاله Intermetallic compounds, XRD, Bond strength, CRB process
نویسندگان مقاله a شعبانی | a. shabani
dep. of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

محمدرضا طرقی نژاد | m r toroghinejad
dep. of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

a شفیعی | a. shafyei
dep. of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran.

سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-738-1&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات