Iranian Journal of Materials Science and Engineering، جلد ۱۳، شماره ۲، صفحات ۲۰-۲۸
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی EVALUATION OF PRECIPITATION HARDENING HEAT TREATMENT OF PH 17-7 STAINLESS STEEL SPRING
چکیده انگلیسی مقاله In this paper, the influence of heat treatment on PH17-7 stainless steel spring was evaluated. Precipitation hardening phenomenon of PH 17-7 steel was evaluated in three stages. First, the spring constant changes with time and temperature was evaluated. Second, the spring constant changes with respect to its original length at constant temperature and time with blocking (spring length after compression, 18 and 21 mm) were investigated. And finally, the spring heat treatment at 480 °C for 80 min and then holding at 230 °C in oil bath for 60 min without blocking were investigated. The results showed that the use of 18 mm block have large spring constant than 21 mm block. The optimal conditions (480°C for 80 min) for this spring to reaching maximum spring constant were determined.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علی اکبر باباکوهی اشرفی | a a babakoohi ashrafi
metallurgical - material engineering department of semnan university

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

h محمدی | h. mohammadi
mining and metallurgical engineering department of amirkabir university


a حبیب الله زاده | a habibolla zade
metallurgical - material engineering department of semnan university

سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-314-2&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات