Iranian Journal of Materials Science and Engineering، جلد ۱۳، شماره ۲، صفحات ۱۰-۱۹
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی IN SITU FABRICATION OF Al 2024-Mg2Si COMPOSITE BY SPARK PLASMA SINTERING OF REACTIVE MECHANICALLY ALLOYED POWDER
چکیده انگلیسی مقاله In situ Al2024- Mg2Si composite was fabricated by spark plasma sintering (SPS) of reactive powder. Reactive powder was obtained from mechanical alloying (MA) of elemental powders. Clad layers of in situ composite were fabricated on Al substrates by spark plasma sintering (SPS). Structural evolution during MA process and after SPS was investigated by X-ray diffractometery (XRD). Scanning electron microscopy (SEM) was utilized to study the microstructure of sintered samples. Hardness and tensile behavior of sintered samples were investigated. The results showed that SPS of mechanically alloyed unreacted powder can result in the in situ formation of Mg2Si and Mg2Al3 within the Al matrix. SPSed clad layer showed a sound and clear interface to the Al substrate with a hardness of about 140 HV. Sintered in situ composite exhibited a tensile strength of 288 MPa.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله z صادقیان | z. sadeghian
ahvaz, 6135743337, iran


r dezfulizadeh | r. dezfulizadeh
ahvaz, 6135743337, iran
نشانی اینترنتی http://ijmse.iust.ac.ir/browse.php?a_code=A-10-975-1&slc_lang=en&sid=en
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده گروه مهندسی مواد . مباحث ویژه
نوع مقاله منتشر شده Research paper