Iranian Journal of Materials Forming، جلد ۲، شماره ۱، صفحات ۴۳-۵۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Interaction Between Precipitation and Dynamic Recrystallization in HSLA-100 Microalloyed Steel
چکیده انگلیسی مقاله Strain induced precipitation in HSLA-100 steel was investigated by conducting hotcompression and relaxation tests at temperature range of 850°C to 1100°C and strain rate of 0.001s-1 to 1s-1. The absence of dynamic recrystallization at temperatures below 1000°C was attributedto the influence of dynamic precipitation. The stress relaxation tests showed that strain inducedprecipitation is possible over a wide range of temperatures from 850°C to 1050°C. The startingand finishing times of precipitation were sensitive to temperature than strain rate. At temperaturerange of 950-1000°C and strain rate of 0.1s-1 the lowest times for precipitation were observed. Thecombination of precipitation-time-temperature and recrystallization-time temperature diagramsshowed that at high temperatures and low strain rates, precipitation precedes dynamicrecrystallization, whereas at the opposite condition, dynamic recrystallization goes in advance. Thestarting and finishing times for dynamic precipitation were approximated about 40 percent lowerthat those for strain induced precipitation.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله غلامرضا ابراهیمی | g r
department of materials and polymer engineering, hakim sabzevari university, sabzevar, iran
سازمان اصلی تایید شده: دانشگاه حکیم سبزواری (Hakim sabzevari university)

a مومنی |
department of materials science and engineering, hamedan university of technology, hamedan, iran

h اسکندری |
department of civil engineering, faculty of engineering, hakim sabzevari university, sabzevar, iran
سازمان اصلی تایید شده: دانشگاه حکیم سبزواری (Hakim sabzevari university)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_2914_c27c2fa1b56c6c556244f2da63ef2da0.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات