Iranian Journal of Materials Forming، جلد ۲، شماره ۱، صفحات ۱۸-۲۹
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Hot Deformation Behavior of Ni80A Superalloy During Non-Isothermal Side Pressing
چکیده انگلیسی مقاله In the present study, the microstructural changes of a Nickel based superalloy Nimonic80A during a non-isothermal deformation were studied. Therefore, microstructure evolutionduring hot side pressing test was predicted with combined methods of finite element analysis andprocessing map of the material. The predicted results were validated through experimentalmicrostructural studies. The results show that the distribution of deformation parameters (i.e.strain, strain rate, and temperature) is non-uniform in the deformed samples. The severity of thisnon-uniformity depends on the amount of sample reduction. High reduction value at one stepforging can cause flow localization and non-uniform dynamic recrystallization, which results theformation of adiabatic shear bands, while using the lower reduction value at each forging step,leads to more uniformly distribution of the deformation parameters and thus uniform the dynamicrecrystallization with the stable flow. Hence the workability and microstructure of the Nimonic80A alloy are mainly depends on the deformation path.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m سیدصالحی | seyed salehi
department of materials science and engineering, k. n. toosi university of technology, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

n anjabin |
department of materials science and engineering, school of engineering, shiraz university, shiraz, iran
سازمان اصلی تایید شده: دانشگاه شیراز (Shiraz university)

r منصوری |
research and development center, turbine machine middle east co., tehran, iran

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_2912_a611e89a3e6895cb3b70ca68597d7d6f.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات