عنوان انگلیسی Optimization of thermomechanical parameters to produce an ultra-high strength compressor disk
چکیده انگلیسی مقاله Structural steels with very high strength levels are often referred to as ultrahigh-strength steels (UHSS). The usage of UHSS has been extensively studied in aerospace industries and offshore platforms. In this study, medium carbon low alloy steel (AMS6305) was thermomechanicaly treated to obtain an ultra-high strength bainitic steel for aircraft engine compressor disk. A novel themomechanical treatment was introduced to optimize microstructure and mechanical properties. By replacing the common quench-temper microstructure of compressor disk with bainite microstructure, an ultra-high strength bainitic steel was achieved. Based on the results obtained, the final microstructures following pre-deformation and subsequent heat treatment showed a very good combination of strength and toughness. Furthermore, it has been shown that austempering time and temperature play a major role in achieving ultra-high strength bainitic steels. The optimized strength and toughness was achieved by up quenching treatment. This is due to partitioning of prior austenite grains by tempered martensite plates.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m آقایی خفری | aghaie khafri
faculty of materials science and engineering, k.n. toosi university of technology, postal code 1999143344, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

محمدحسین شیخ انصاری | m h sheikh ansary
faculty of materials science and engineering, k.n. toosi university of technology, postal code 1999143344, tehran, iran
سازمان اصلی تایید شده: دانشگاه صنعتی خواجه نصیرالدین طوسی (Khajeh nasir toosi university of technology)

نشانی اینترنتی http://ijmf.shirazu.ac.ir/article_3273_4cb96e29d4893a0c2ab2ad41644b6b76.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات