International Journal of Iron and Steel Society of Iran، جلد ۲، شماره ۱، صفحات ۱-۶
عنوان فارسی Shot Peening as an Alternative to Fatigue Life Improvement of CK۴۵ Steel Coated with an Electroless Ni-Cu-P
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Shot Peening as an Alternative to Fatigue Life Improvement of CK45 Steel Coated with an Electroless Ni-Cu-P
چکیده انگلیسی مقاله The effect of an electroless Ni-Cu-P coating on the fatigue behavior of quenched and tempered CK45 steel has been investigated. The fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. The results indicate that plating of the base steel leads to a fatigue life reduction. The decrease in the fatigue strength was observed to be less marked for the shot peened specimens. The microscopic observations indicate that in the as-deposited condition, the reduction in fatigue life is associated with the nucleation of fatigue cracks on the lateral side of coating. On the contrary, when the samples were shot peened prior to the coating deposition, the crack initiation sites were displaced to the coating-substrate interface which led to an improvement of fatigue behaviour
کلیدواژه‌های انگلیسی مقاله Electroless Ni-Cu-P deposit, Fatigue, Shot peening, CK45 steel, Coating
نویسندگان مقاله t سعید |
faculty of materials engineering, sahand university of technology, p.o. box 51335 1996, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

s یزدانی |
faculty of materials engineering, sahand university of technology, p.o. box 51335 1996, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

n پروینی احمدی | parvini ahmadi
faculty of materials engineering, sahand university of technology, p.o. box 51335 1996, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://journal.issiran.com/article_4779_efd6ee366c0e6632ed3fc9b8e4ec5cf2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات