International Journal of Iron and Steel Society of Iran، جلد ۲، شماره ۲، صفحات ۳۶-۴۲
عنوان فارسی Recrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Recrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
چکیده انگلیسی مقاله In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has been applied to cold rolled samples and the resulted microstrucrures have been compared with the microstructure obtained from the box annealing process in MSP. It is found that at 635 and 700ºC the isothermal annealing produces equiaxed grains, while box annealing process presents an elongated grain structure. The recrystallization fractions have been measured using the point counting method. The linear intercept method has been employed to measure the grain size. It is revealed that at 550ºC, in salt bath annealing, recrystallization is stopped after 50% recrystallization with elongated new grains. Constant grain sizes upon holding after recrystallization at 635 and 700ºC during isothermal annealing show that the grain growth is stopped. Further holding at 700ºC results an abnormal grain growth in the recrystalized microstructure. The hardness variations during annealing, with a decrease at the beginning of annealing followed by an increase trend at all temperatures, show a good consistency with microstructural observations. Investigation of the results leads to the conclusion that a precipitation process occurs during annealing which greatly affects both restoration processes and resulted microstructure as well as the properties. The effect of the precipitation process depends on the time of its occurrence with respect to each restoration process. A Relatively high value of 315 KJ/mole for recrystallization activation energy has been related to the simultaneous occurrence of recrystallization and precipitation processes.
کلیدواژه‌های انگلیسی مقاله Low carbon steel, Recrystallization, Mirostructure, Gain growth, Pecipitation, Mobarakeh
نویسندگان مقاله b سلیمانی امیری | soleimani amiri
department of metallurgy, shahid bahonar university, kerman, iran
سازمان اصلی تایید شده: دانشگاه شهید باهنر (Shahid bahonar university)

غلامحسین اکبری | g h
international center for science and high technology and environmental science, kerman, iran

نشانی اینترنتی http://journal.issiran.com/article_4791_467968202ea2d5d9e8f9c95f7852c15c.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات