International Journal of Iron and Steel Society of Iran، جلد ۲، شماره ۲، صفحات ۳۰-۳۵
عنوان فارسی High Temperature Behavior of Dual Phase Steels
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی High Temperature Behavior of Dual Phase Steels
چکیده انگلیسی مقاله Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 4500C and then decreased at higher temperatures. At a given temperature, yield stress, tensile strength, and work hardening increased with increasing volume fraction of martensite. Similar behavior was observed by changing martensite morphology from network to fibrous martensite. The change in mechanical properties was related to the effects of dynamic strain aging, high temperature softening, and martensite tempering.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a اکرامی |
department of materials science and engineering, sharif university of technolog, tehran, iran

m bahrehbarpoor |
department of materials science and engineering, sharif university of technolog, tehran, iran

نشانی اینترنتی http://journal.issiran.com/article_4790_d0cc92124f0a3aed88e80cf4c243dea2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات