International Journal of Iron and Steel Society of Iran، جلد ۲، شماره ۲، صفحات ۱-۸
عنوان فارسی Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing ۰.۴۸% and ۴.۸۸% Al
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing 0.48% and 4.88% Al
چکیده انگلیسی مقاله The influence of aluminium on the microstructure of austempered ductile cast iron (ADI) has been studied. The presence of well distributed graphite in the matrix, and a relatively high volume fraction of retained austenite are responsible for the good mechanical properties of the Aluminium alloyed austempered ductile irons including excellent wear resistance, higher resistance to thermal shock, better graphitising tendency and higher resistance to oxidation at high temperatures. A number of specimens of different composition have been made by green sand-casting and gravity die-casting. The transformation to a bainitic microstructure during austempering under different conditions was then examined for the most successful experimental casts. Austenitising temperature of 920°C, and austempering temperatures of 350°C at different holding times have been used. Microstructures have been examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Furthermore, it was found that isothermal transformation at 350°C for different soaking times gave a typical bainitic microstructure. Extension of isothermal transformation time leads to precipitation of carbides which also depends on the Al concentration.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله علیرضا علیرضا کیانی رشید | a r kiani rashid
department of materials engineering, university of sistan amp;amp; baluchestan, zahedan, iran

d v edmonds | d v
department of materials, university of leeds, leeds, uk

نشانی اینترنتی http://journal.issiran.com/article_4786_766cd962b8e28477132a9edf479c85ee.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات