International Journal of Iron and Steel Society of Iran، جلد ۳، شماره ۱، صفحات ۸-۱۲
عنوان فارسی Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel
چکیده انگلیسی مقاله Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancked structure. When Z values decreased, the flow curves displayed DRX in two ways: single peak behavior observed at low Z values and multiple peak behavior at the lowest ones. In addition, the peak strain, εp, necessary for DRX is also determined as a function of peak stress, sp, and Z. According to the observed and calculated data, at low sp values, εp is directly proportional to sp, while in higher amounts, εp rarely depends on it. Besides, εp expotenentially depends on Z.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله a شکوه فر |
faculty of mechanical engineering, khajenasir toosi university of technology, tehran, iran

سید محمد عباسی | s m
faculty of mechanical engineering, khajenasir toosi university of technology, tehran, iran

n ehseni |
faculty of material engineering, mut, tehran, iran

نشانی اینترنتی http://journal.issiran.com/article_4806_282f0c806f74e286b2cea3fff4e2d3d9.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات