عنوان فارسی Investigations of Calcium Aluminate Slag Penetration to MgO Monolithic Refractories in Steelmaking Process
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Investigations of Calcium Aluminate Slag Penetration to MgO Monolithic Refractories in Steelmaking Process
چکیده انگلیسی مقاله In this study, slag penetration into a magnesia refractory monolithic was investigated by the crucible test method. A synthetic calcium aluminate slag system has been used to study commercial magnesia mix refractory for 1, 2, 3, 4, 5 and 6 hours at 1450°C and 1600°C.
It has been shown that the penetration rate is controlled by a diffusion mechanism at 1450°C. In this case, capillaries are the main channels of initial slag penetration into the refractory. In the penetration process of the slag system, calcium silicate was formed on the surfaces of MgO grains at 1450°C and around them by reaction between grain boundary and mayenite, as a main phase of slag with a low melting point.
Dissolution of the refractory components in the slag could be supported by the penetration process at 1600°C. In this case, dissolution of the refractory components in the slag not only makes new open channels, but also changes the local slag composition, resulting in an increase in surface tension and viscosity of the slag.
کلیدواژه‌های انگلیسی مقاله Slag, Magnesia, Calcium aluminate slag, Crucible test method, Corrosion
نویسندگان مقاله محمدحسین امین | m h
material and energy research center, p.o. box 14155-4777 tehran, iran

a کاظم زاده |
material and energy research center, p.o. box 14155-4777 tehran, iran

b ارفعی |
department of mechanical engineering, state university of new york, usa

n سها chaudhury | saha chaudhury
school of materials science and engineering, unsw, sydney, australia

v sahajwalla |
school of materials science and engineering, unsw, sydney, australia

نشانی اینترنتی http://journal.issiran.com/article_4819_e5ebdec4c00776c9f2b9e13a43c1366f.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات