عنوان فارسی Effect of Ti-microalloy Addition on the Formability and Mechanical Properties of a Low Carbon (ST۱۴) Steel
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of Ti-microalloy Addition on the Formability and Mechanical Properties of a Low Carbon (ST14) Steel
چکیده انگلیسی مقاله    A low carbon Al-killed Ti-added steel was produced in Mobarakeh Steel Complex in Iran. Mechanical properties and microstructural characterizations of steel in the as-cast, hot-rolled, cold-rolled and annealed conditions are presented. Dilatometery tests were carried out to measure the finishing and annealing temperatures of steel. It was found that the addition of small amounts of Ti increased the transformation temperatures. In addition, microalloying with titanium improved the ductility of the produced slabs and hot rolled steel sheet. However, low temperature annealing of Ti-added cold-rolled steel sheets led to a decrease in ductility. The results indicate that the full softening of the Ti-added cold-rolled steel is completed for an annealing time of 2hr at 800°C.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m طرقی نژاد |
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

g دینی |
department of materials engineering, isfahan university of technology, isfahan, 8415683111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://journal.issiran.com/article_4813_7bd96343709db08669d906769dd33967.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات