International Journal of Iron and Steel Society of Iran، جلد ۴، شماره ۱، صفحات ۳۹-۴۹
عنوان فارسی A Comparative Evaluation of Welding Consumables for Dissimilar Welds between ۳۱۰ Austenitic Stainless Steel and Inconel ۶۵۷
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی A Comparative Evaluation of Welding Consumables for Dissimilar Welds between 310 Austenitic Stainless Steel and Inconel 657
چکیده انگلیسی مقاله The current work was carried out to characterize welding of AISI 310 austenitic stainless steel to Inconel 657 nickel-chromium superalloy. The welds were produced using four types of filler materials; the nickel-based corresponding to Inconel 82, Inconel A, Inconel 617 and austenitic stainless steels 310. Of the two joints involved, this paper describes the choice of welding consumables for the joint. The comparative evaluation was based on hot cracking tests (Varestraint test) and estimation of mechanical properties. While Inconel A exhibited the highest resistance to solidification cracking, the Inconel 617 filler material also showed moderate resistance and in addition, the latter was superior from the mechanical properties view-points. It was concluded that for the joint between Inconel 657 and 310 SS, the Inconel A filler material offered the best compromise.
کلیدواژه‌های انگلیسی مقاله AISI 310, Inconel 657, Dissimilar Welding, Hot Cracking, Varestraint Test
نویسندگان مقاله h نفاخ |
department of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

m شمعانیان |
department of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

f اشرفی زاده |
department of materials engineering, isfahan university of technology, isfahan, 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://journal.issiran.com/article_4828_8225ace3f1a1397fddbc7d3edd906ed7.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات