این سایت در حال حاضر پشتیبانی نمی شود و امکان دارد داده های نشریات بروز نباشند
International Journal of Iron and Steel Society of Iran، جلد ۴، شماره ۱، صفحات ۳۴-۳۸
عنوان فارسی The Effect of Surface Treatment on Corrosion behavior of Surgical ۳۱۶L Stainless Steel Implant
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Effect of Surface Treatment on Corrosion behavior of Surgical 316L Stainless Steel Implant
چکیده انگلیسی مقاله The AISI 316 L Stainless Steel (SS) specimens were exposed to passivation surface through two different processes including; holding in 40-vol% HNO3 at temperature of 60 ºC for 30 min and 15-vol%H2SO4 at ambient temperature for 1 hour. The corrosion behavior of specimens was evaluated in physiological solutions by electrochemical in vitro tests through linear and Tafel polarization tests. Cyclic polarization tests were performed for investigating of the specimen’s resistance against pitting. Finally, the corrosion resistance of untreated and modified specimens was compared. The results show that the corrosion resistance of 316L SS metallic implant is increased due to passivation surface treatment.
 
کلیدواژه‌های انگلیسی مقاله Surgical Implant, 316L stainless steel, Corrosion behavior, Surface Treatment, Biocompatibility
نویسندگان مقاله a پارساپور |
department of materials engineering, isfahan university of technology, isfahan 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

محمدحسین فتحی | m h
department of materials engineering, isfahan university of technology, isfahan 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

m صالحی |
department of materials engineering, isfahan university of technology, isfahan 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

a ساعتچی |
department of materials engineering, isfahan university of technology, isfahan 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

m مهدیخانی |
department of materials engineering, isfahan university of technology, isfahan 84156-83111, iran
سازمان اصلی تایید شده: دانشگاه صنعتی اصفهان (Isfahan university of technology)

نشانی اینترنتی http://journal.issiran.com/article_4827_4112f5f21a19a17aa19c28ee25f59376.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات