عنوان فارسی Investigation of Transformation Induced Plasticity in High Al–low Si TRIP Steel
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Investigation of Transformation Induced Plasticity in High Al–low Si TRIP Steel
چکیده انگلیسی مقاله This study was conducted in order to investigate the influence of plastic deformation on the transformation of retained austenite in a TRIP steel with a high content of Al and a low content of Si. To the aim, appropriate treatments were used to produce the starting material (TRIP steel). The microstructure of the obtained steel was composed of bainite and phases including ferrite and retained austenite. Afterwards, 40 % plastic deformation was applied to the starting material using a rolling machine. Microhardness test, microstructural investigations and determination of volume fraction of retained austenite by x-ray diffraction method before and after 40% cold work demonstrated that the volume fraction of retained austenite in the starting material was decreased as the plastic deformation was increased. During the plastic deformation, large grains of retained austenite were transformed to martensite while the small ones tended to be stable.
کلیدواژه‌های انگلیسی مقاله TRIP steel, Retained austenite, transformation
نویسندگان مقاله h moosalu |
department of materials engineering, sahand university of technology, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

a نوری teymorlu | noori teymorlu
department of materials engineering, sahand university of technology, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

n پروینی احمدی | parvini ahmadi
department of materials engineering, sahand university of technology, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

s یزدانی |
department of materials engineering, sahand university of technology, tabriz, iran
سازمان اصلی تایید شده: دانشگاه صنعتی سهند (Sahand university of technology)

نشانی اینترنتی http://journal.issiran.com/article_6515_e1d5be7d2bcea07c966d580257413d81.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات