International Journal of Iron and Steel Society of Iran، جلد ۱۲، شماره ۱، صفحات ۳۷-۴۱
عنوان فارسی The Role of SiC and Different Binders on Mechanical Strength and Compaction of Silica Based Refractories Materials
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Role of SiC and Different Binders on Mechanical Strength and Compaction of Silica Based Refractories Materials
چکیده انگلیسی مقاله Silica refractory bricks are used especially in the metallurgical industries, due to desirable properties such as high melting point, rigidity, and high temperatures strength. In this research, different amount of SiC were added to Silica refractory containing different binders such as Borax, Boric acid, Calcium nitride, Sodium tri poly phosphate, Sodium hexa meta phosphate (SHMP) and lime. Physical properties (density and porosity), mechanical properties (cold crush strength, CCS) and microstructure were studied. This study indicated that SiC improves the physical and mechanical properties. In general, increasing SiC with different binders improve the mechanical and compaction in the samples. Silica refractory sample containing 20 %wt. SiC and 5 % wt. borax as a binder had the best results of mechanical strength and compaction. In this sample, glassy phases fill the voids and increase temperature between particles. In fact, glass phase formation increases compaction, density, and strength.
کلیدواژه‌های انگلیسی مقاله AISI 1060 Steel, Tempering, Hardness, Tensile, Fatigue
نویسندگان مقاله e کرمیان |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

h قیصری |
department of mechanical and material, lenjan branch, islamic azad university, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

v کدخدایی |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a منشی |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

نشانی اینترنتی http://journal.issiran.com/article_14436_ed9a2eede8e02587f71eab9dc698ba40.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات