International Journal of Iron and Steel Society of Iran، جلد ۱۳، شماره ۱، صفحات ۲۰-۲۶
عنوان فارسی The Influence of Hematite on High Speed Continuous Casting of Steel Lubricating Powders: Viscosity and Crystallization
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی The Influence of Hematite on High Speed Continuous Casting of Steel Lubricating Powders: Viscosity and Crystallization
چکیده انگلیسی مقاله Mold powders used in the continuous casting of steel contain the harmful CaF2 as a main substance developing toxic gases such as SiF4 and HF at elevated temperatures. In this study, three samples of I1, I2 and I3, which contained gypsum free Portland cement clinker with different percentages of Fe2O3 (5.68, 6.83, 8.02 ) and F- (2.09, 1.06, 0), were prepared and their main characteristics were compared with those of the standard and the molten reference powder. The results showed similarity in viscosity between samples I1, I2 and the molten reference powder, which was desired. Sample I3 with no fluorine showed a higher viscosity in comparison to the standard sample and therefore, a complete replacement of CaF2 with Fe2O3 could not be recommended. Furthermore, the XRD of the reference powder, molten reference powder and sample I2, the SEM of the molten reference powder and sample I2 and EDS of sample I2 analyses were also performed. The XRD patterns results demonstrated that by decreasing CaF2, cuspidine phase was vanished, while other crystalline phases such as gehlenite, fayalite, akermanite, nepheline and Mn3O4 were found. In addition, SEM micrographs and EDS analysis of sample I2 in the white area revealed crystalline particles in the glass matrix. Considering EDS analysis of sample I2 showed the existence of Mg, Na, Mn, Fe, Si, Al and O. It could be concluded that such crystals as gehlenite, akermanite, nepheline and fayalite were composed in the glass matrix, developing to similar heating properties in the glassy matrix. 
کلیدواژه‌های انگلیسی مقاله Mold powder, Viscosity, Fluorine, Hematite
نویسندگان مقاله a شفیعی راد |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a عارف پور |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a منشی |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

a سعیدی |
advanced materials research center, faculty of materials engineering, najafabad branch, islamic azad university, najafabad, isfahan, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

نشانی اینترنتی http://journal.issiran.com/article_20873_b298ae5318d40ad5bc4b3af68743e5e2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده fa
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات