Evaluation of Retention of two Different Cast Post-Core Systems and Fracture Resistance of the Restored Teeth |
|
| چکیده انگلیسی مقاله |
Statement of the Problem: The survival of pulpless teeth restored with different post and core systems is still a controversial issue. Purpose: This study compared the retention of two different post and core systems and also the fracture resistance of teeth restored with these systems. Material and Method: Eighty endodontically treated maxillary central incisors were sectioned perpendicular to the long axis at a point 2mm incisal to the cemento-enamel junction (CEJ) and then the root canals were obturated. The restored teeth were randomly divided into two equal groups of 40. One group was restored with Nickel-Chromium (Ni-Cr) post and core system and the other group with Non-Precious Gold alloy (NPG) system. For evaluation of fracture resistance of the restored teeth, the specimens (n=20 per each group) were mounted in acrylic resin blocks and a layer of polyvinyl siloxane was applied to cover the roots. Loads were applied at an angle of 45 degrees to the long axis of the teeth and measured with a universal testing machine. The axial retention values of the studied groups (no=20) were measured on an Instron testing machine at a crosshead speed of 0.5 mm/min. Statistical analyses were performed using SPSS version 19.00 and student’s t-test (α=0.05). Results: Although retention failure load for Ni-Cr system was lower than NPG system, there was no significant difference between the two systems ( p = 0.7). However, fracture resistance of the teeth restored with Ni-Cr post and core system was significantly higher than NPG group ( p = 0.000). Conclusion: There was no significant difference between the retention of the studied post and core systems. Although significantly higher fracture thresholds were recorded for Ni-Cr post and core group, the failure loads of both systems may rarely occur clinically. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
امیر علی رضا خالدی | amir ali reza khaledi
dept. of prosthodontic, school of dentistry, shiraz university of medical sciences, shiraz, iran.
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
شکوفه شیخیان | shekufe sheykhian
students’ research committee, school of dentistry, international branch, shiraz university of medical sciences, shiraz, iran.
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
آرش خدایی | arash khodaei
students’ research committee, school of dentistry, international branch, shiraz university of medical sciences, shiraz, iran.
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
|
|
| نشانی اینترنتی |
http://dentjods.sums.ac.ir/index.php/JDSUMS/article/view/1092 |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
Original Article |
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|