عنوان انگلیسی Aligned and random nanofibrous nanocomposite scaffolds for bone tissue engineering
چکیده انگلیسی مقاله Aligned and random nanocomposite nanofibrous scaffolds were electrospun from polycaprolactone (PCL), poly (vinyl alcohol) (PVA) and hydroxyapatite nanoparticles (nHA). The morphology and mechanical characteristics of the nanofibers were evaluated using scanning electron microscopy and tensile testing, respectively. Scanning electron microscopy revealed fibers with an average diameter of 123 ± 32 nm and 339 ± 107 nm for aligned and random nanofibers, respectively. The mechanical data indicated the higher tensile strength and elastic modulus of aligned nanofibers. The in vitro biocompatibility of aligned and random nanofibrous scaffolds was also assessed by growing mesenchymal stem cells (MSCs), and investigating the proliferation and alkaline phosphatase activity (ALP) on different nanofibrous scaffolds. Our findings showed that the alignment orientation of nanofibers enhanced the osteogenic differentiation of stem cells. The in vitro results showed that the aligned biocomposite nanofibrous scaffolds of PCL/nHA/PVA could be a potential substrate for tissue engineering applications, especially in the field of artificial bone implant.
کلیدواژه‌های انگلیسی مقاله Electrospinning, Nanofibers, Bone tissue engineering
نویسندگان مقاله امیر doustgani | amir doustgani
biotechnology group, chemical engineering department, tarbiat modares university, tehran, iran

سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

ابراهیم واشقانی فراهانی | ebrahim vasheghani farahani
biotechnology group, chemical engineering department, tarbiat modares university, tehran, iran

سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

مسعود سلیمانی | masoud soleimani
department of hematology, faculty of medicine, tarbiat modares university, tehran, iran

سازمان اصلی تایید شده: دانشگاه تربیت مدرس (Tarbiat modares university)

نشانی اینترنتی http://nmj.mums.ac.ir/article_699.html
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده 1
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات