Nanomedicine Journal، جلد ۲، شماره ۳، صفحات ۲۰۳-۲۱۰
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Preparation and characterization of Sr-Ti-hardystonite (Sr-Ti-HT) nanocomposite for bone repair application
چکیده انگلیسی مقاله Objective(s): Hardystonite (HT) is Zn-modified silicate bioceramics with promising results for bone tissue regeneration. However, HT possesses no obvious apatite formation. Thus, in this study we incorporated Sr and Ti into HT to prepare Sr-Ti-hardystonite (Sr-Ti-HT) nanocomposite and evaluated its in vitro bioactivity with the purpose of developing a more bioactive bone substitute material. Materials and methods:The HT and Sr-Ti-HT were prepared by mechanical milling and subsequent heat treatment. Calcium oxide (CaO), zinc oxide (ZnO) and silicon dioxide (SiO2) (all from Merck) were mixed with molar ratio of 2:1:2. The mixture of powders mixture was then milled in a planetary ball mill for 20 h. In the milling run, the ball-to-powder weight ratio was 10:1 and the rotational speed was 200 rpm. After synthesis of HT, 3% nanotitanium dioxide (TiO2, Degussa) and 3% strontium carbonate (SrCO3, Merck) were added to HT and then the mixture was ball milled and calcined at 1150°C for 6 h. Simultaneous thermal analysis (STA), X-ray diffraction (XRD), Transmission electron microscopy (TEM) and Fourier transform infra-red spectroscopy (FT-IR) performed to characterize the powders. Results:XRD and FT-IR confirmed the crystal phase and silicate structure of HT and TEM images demonstrated the nanostructure of powders. Further, Sr-Ti-HT induced apatite formation and showed a higher human mesenchymal stem cell (hMSCs) adhesion and proliferation compared to HT. Conclusion:Our study revealed that Sr-Ti-HT with a nanostructured crystal structure of 50 nm, can be prepared by mechanical activation to use as biomaterials for orthopedic applications.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله حسین محمدی | hossein mohammadi
department of biomaterials, science and research branch, islamic azad university, yazd, iran

سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

مسعود حافظی | masoud hafezi
biomaterials group, nanotechnology and advanced materials department, materials and energy research center, alborz, iran |pardis pajoohesh fanavaran yazd, bt center, yazd science and technology park, yazd, iran


سعید حصارکی | saeed hesaraki
biomaterials group, nanotechnology and advanced materials department, materials and energy research center, alborz, iran


محمد مجید sepantafar | mohammad majid sepantafar
department of stem cell and developmental biology at cell science research center, royan institute for stem cell biology and technology, acecr, tehran, iran

سازمان اصلی تایید شده: پژوهشگاه رویان (Royan institute)

نشانی اینترنتی http://nmj.mums.ac.ir/article_4476.html
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده 1
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات