K, Ca, and Zn Ratios Affect Glass Frit Properties |
|
| چکیده انگلیسی مقاله |
Frites with mole fractions of 2.5 SiO₂, 0.20 Al₂O₃, 0.15 B₂O₃, 0.15 ZnO, 0.17 K₂O, and 0.67 CaO were studied at three different S ratios—0.37 (denoted as F1 frits), 0.31 (F2), and 0.24 (F3)—where S = K₂O / (CaO + ZnO). ZnO powders of two different particle sizes were used as raw materials: 500 nm (N series), obtained from recycled Zn ingot dust, and >1 μm (F series), sourced from commercial ZnO. Upon decreasing the S ratio, the molar volumes of the frits decreased. The glass transition temperature difference (ΔTg = –154 °C) decreased, whereas the crystallization temperature difference (ΔTp = +17 °C) increased. It was shown that the glass stability (GS) values were independent of ZnO powder size, although the molar volumes of the N series were lower than those of the F series. Crystalline phases identified in the resulting glazes included zinc silicate (willemite), anorthite, and parawollastonite. The hardness values ranged between 700 and 850 Hv, while the glazes exhibited transparency and whiteness values exceeding 80 and 60, respectively. |
|
| کلیدواژه‌های انگلیسی مقاله |
Glaze,ZnO,size,Frites,TEC |
|
| نویسندگان مقاله |
Aida Faeghinia |
Associate Professor, Department of Ceramic, Materials and Energy Research Center, Karaj, Iran.
Zahra Khakpour |
Assistant Professor, Department of Ceramic, Materials and Energy Research Center, Karaj, Iran.
R. Salami |
MSc, Department of Ceramic, Materials and Energy Research Center, Karaj, Iran.
Mohamad Zakeri |
Associate Professor, Department of Ceramic, Materials and Energy Research Center, Karaj, Iran.
|
|
| نشانی اینترنتی |
https://www.acerp.ir/article_225920_811a44013b6fcbd062e0850ca2a90c6f.pdf |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|