Preparation, Characterization and Catalytic Testing over Bimetallic Pt-Pd/HZSM-5 Catalysts in NO Reduction by Propylene |
|
| چکیده انگلیسی مقاله |
Bi-functional and bi-metallic ZSM-5 catalysts with different noble metal mass ratios were prepared using the deposition-precipitation method and ionic exchange with NH4+. Systemic XRD, BET/BJH, STEM, and XPS spectroscopy investigations of the structural and electronic properties of these catalysts showed that 2⁓3-nm Pt and Pd metallic nanoparticles were highly dispersed over the ZSM-5 support, with strong interactions between Platinum and Palladium, and a good distribution of the acid sites on the surface of the catalysts which have been observed using the FTIR method by adsorption of pyridine. Considering optimized values of NO/C3H6 ratio=1 and GHSV= 22000 h-1, some parameters, acidity, temperature, surface morphology, and catalytic activity performance of Pd-Pt/HZSM-5 zeolites were investigated in the selective catalytic reduction of NO by C3H6, Pd-Pt/HZSM-5 bi-functional catalysts exhibited improved catalytic properties relative to their monometallic counterparts. The results show that the active components are uniformly dispersed and distribute well in the micro-porous support. For the Pt0.6Pd0.4/HZSM-5 catalyst, the maximum conversion of NO to N2 approached 63% at 450 ºC with 100% N2 selectivity. By contrast, for
the 1%Pt/HZSM-5 catalyst, the maximum NO conversion to N2 reached 52% at 450 ºC and only 42% for 1%Pt/HZSM-5. The Pt0.6Pd0.4/ZSM-5 catalyst also exhibited high durability and catalytic activity at high reaction temperatures. |
|
| کلیدواژه‌های انگلیسی مقاله |
HZSM-5 catalyst,bimetallic Pt-Pd,NO reduction,C3H6-SCR,Catalytic activity |
|
| نویسندگان مقاله |
Mounir Sakmeche |
Laboratory of Catalytic Materials and Industrial Processes (LMPCI) Department of Hydrocarbos and Renewable Energies, Faculty of Science and Technology. University of Adrar, National Highway No. 06. Adrar 01000, ALGERIA
Elfahem Sakher |
Department of Chemistry, Faculty of Science and Technology, University of Adrar, National Highway No. 06. Adrar 01000, ALGERIA
Billel Smili |
Laboratory of Catalytic Materials and Industrial Processes (LMPCI) Department of Hydrocarbons and Renewable Energies, Faculty of Science and Technology. University of Adrar, National Highway No. 06. Adrar 01000, ALGERIA
Mohamed El Amine Dahou |
Laboratory of Catalytic Materials and Industrial Processes (LMPCI) Department of Hydrocarbons and Renewable Energies, Faculty of Science and Technology. University of Adrar, National Highway No. 06. Adrar 01000, ALGERIA
Ahmed Belhakem |
Department of Chemistry, University of Mostaganem, B.P 1001, 27000 Mostaganem, ALGERIA
Leila Belgacem |
Research Center in Industrial Technologies CRTI, Cheraga 16014, Algiers, ALGERIA
Mohammed Messaoudi |
Department of Biological Sciences, Faculty of Natural and Life Sciences, University of Adrar, ALGERIA
Samira Benhara |
Research Center in Industrial Technologies CRTI, Cheraga 16014, Algiers, ALGERIA
|
|
| نشانی اینترنتی |
https://ijcce.ac.ir/article_712116_7e79d1732e7f347b9d5dea13acd40a31.pdf |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|