Iranian Journal of Materials Forming، جلد ۱۰، شماره ۴، صفحات ۲۵-۳۳
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of Heat Treatment and Rolling on the Microstructure and Tensile Behavior of Twin-Roll Cast AA8006 Aluminum Foils
چکیده انگلیسی مقاله The Microstructure and tensile properties of 60 μm thick AA8006 aluminum foil were investigated in the present study. Sheets of AA8006 were produced by twin-roll casting (TRC) with a thickness of 8 mm and were reduced to 4.5 mm thickness by one pass of rolling. The sheets were heat-treated, homogenized and annealed. After heat treatment, both processes were subjected to cold rolling to compare their tensile properties in 60 µm thickness after final annealing at different temperatures. The results showed that after homogenization, the short rod like eutectic phase is dispersed homogeneously in Al matrix of homogenized TRC processed alloy. The EDS results show that the contents of iron and manganese elements in the eutectic phase of TRC processed alloys decrease after homogenization, with the difference that this decrease is more noticeable in the thickness of 4.5 mm after annealing. It was also found that the homogenized sheet with a thickness of 60 micrometers after a rolling step was compared to the homogenized sheet after casting, due to smaller spherical intermetallic particles and better grain structure after heat treatment, the relative elongation from 12% to 27.5% showed an increase.
کلیدواژه‌های انگلیسی مقاله aluminum, Rolling, Microstructure, Mechanical properties
نویسندگان مقاله M. Talebi |
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran

A. R. Eivani |
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran

S.M.A. Boutorabi |
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran

نشانی اینترنتی https://ijmf.shirazu.ac.ir/article_7470_6dca34abce5de06642b465ab08b5a659.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات