Physical Chemistry Research، جلد ۱۱، شماره ۲، صفحات ۳۱۵-۳۲۶
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی RSM Optimized Adsorption of Eriochrome Black T Dye onto Alumina Nanoprticles: Isotherm and Kinetics Studies
چکیده انگلیسی مقاله Nanoparticles materials with good structural properties can serve as an excellent candidate for the remediation of wastewater. In this study, mesoporous gamma-alumina was synthesized from kaolin using polyoxyethylene (40) stearate (PS) surfactant. The XRD diffractogram of the alumina revealed broad peaks that signifies small crystallites, while the FTIR spectrum indicates that the alumina possessed both tetrahedral and octahedral structure. The surface area, average pore diameter, and pore volume obtained from the N2-sorption study are respectively 76.0 m2/g, 4.4 nm, and 0.14 cm3/g. The XRF result revealed up to 98% Al2O3 composition, indicating a very high purity of the alumina. The alumina (Nano-Al) was applied for the adsorption of Eriochrome Black T dye, and the process optimized using RSM analysis by Box-Behnken Design (BBD) model. From the optimization results, the model's R2 (0.8736) value implies 87.36% on the percent dye removal could be due to the variation in the independent variable. While the F-value of 7.68 implies the model is significant. Consequently, 98.2% dye removal was achieved under the optimum conditions. This may be attributed to the enhanced structural properties of the Nano-Al. The experimental data were fitted to Langmuir isotherm, and the adsorption kinetics data were fitted to pseudo-second-order model.
کلیدواژه‌های انگلیسی مقاله Mesoporous alumina,Adsorption,optimization,Dye
نویسندگان مقاله Abdu Muhammad Bello |
Department of Chemistry, Faculty of Sciences, Kano University of Science and Technology Wudil, PMB 3244, Kano State, Nigeria

Naziru Alhassan Muhammad |
Department of Chemistry, Faculty of Sciences, Kano University of Science and Technology Wudil, PMB 3244, Kano State, Nigeria

Abubakar Hamisu |
Department of Chemistry, Faculty of Sciences, Kano University of Science and Technology Wudil, PMB 3244, Kano State, Nigeria

نشانی اینترنتی https://www.physchemres.org/article_152851_b92b18be89810323a1516790cca694c3.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات