Journal of Nanostructures، جلد ۱۰، شماره ۳، صفحات ۶۳۹-۶۵۱
عنوان فارسی
چکیده فارسی مقاله
کلیدواژه‌های فارسی مقاله
عنوان انگلیسی Effect of alkali strength on the hydrothermal growth of photoactive TiO2 nanowires
چکیده انگلیسی مقاله Titanium dioxide nanowires have been prepared by the alkali hydrothermal treatment of TiO2 nanoparticles in presence of different hydroxides and characterized using transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy dispersive x-ray (EDX), N2 adsorption-desorption measurements, powder x-ray diffraction (XRD) and UV-Vis spectroscopy. Interestingly, only the strong bases (NaOH and KOH) formed mainly anatase titanium dioxide nanowires with the evident collapse of definitive (110) rutile XRD peak. The KOH-based titanium oxide nanowires exhibited comparatively low diameter (∼5 nm), high surface area (228.34 m2/g), and low band gap energy (2.90 eV), and showed the most remarkable photocatalytic degradation (98.87 %). However, the NH4OH-based titanium dioxides were nanoparticles having insignificantly modified morphology and least photocatalytic efficiency. The effect of operating variables on the degradation of aqueous methylene blue (MB) over the obtained alkali hydrothermal TiO2 was studied using response surface methodology, based on a bivariate central composite design (CCD) and optimized numerically.
کلیدواژه‌های انگلیسی مقاله Hydrothermal, TiO2 nanowires, alkali, Methylene blue, CCD
نویسندگان مقاله Abubakar Hamisu |
Department of Pure and Industrial Chemistry, Bayero University Kano, 700241 Kano, Kano State, Nigeria

Umar Gaya |
Department of Pure and Industrial Chemistry, Bayero University Kano, 700241 Kano, Kano State, Nigeria

Abdul Gaya |
Department of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor D.E., Malaysia

نشانی اینترنتی https://jns.kashanu.ac.ir/article_110804_7aceeb85a76b192935638cfdec6584fc.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات