Journal of Ultrafine Grained and Nanostructured Materials، جلد ۵۴، شماره ۱، صفحات ۱۰۱-۱۱۱
|
|
|
عنوان فارسی |
|
|
چکیده فارسی مقاله |
|
|
کلیدواژههای فارسی مقاله |
|
|
عنوان انگلیسی |
Investigation of in-situ synthesis of alumina reinforcement and comparative flexural behavior with respect to ex-situ Al2O3 reinforced copper composite |
|
چکیده انگلیسی مقاله |
Ex-situ and in-situ reinforced copper matrix composite samples containing 1.1 wt. % and 2 wt. % Al2O3 were produced by spark plasma sintering (SPS) at 830 °C and holding time of 30 min. In-situ reinforced sample was synthesized by a novel technique using the reaction between ball-milled copper oxide and Cu-10 wt. % Al filings as the additive and copper powder. The in-situ formation of alumina reinforcement was confirmed by SEM observation and EDS analysis. Morphology and distribution of reinforcement phase in different composite samples were studied. The in-situ reinforced composite sample showed superior flexural fracture strength and strain (349 MPa and 0.027, respectively). Different patterns of crack propagation were observed in the SEM images of fracture surfaces: the reinforcement’s interface path (due to the formation of undesired oxide phase) was dominant in the ex-situ samples, while the interface of in-situ reinforcements remained intact and the cracks originated in the agglomeration sites. |
|
کلیدواژههای انگلیسی مقاله |
in-situ Al2O3 reinforcement, copper matrix composite, Flexural Strength, fracture behavior |
|
نویسندگان مقاله |
Maoud Khodabakhshzade Fallah | Department of Metallurgy & Ceramics, College of Engineering, Mashhad Branch, Islamic Azad University,
Mashhad, Iran
Saeid Ghesmati Tabrizi | Department of Metallurgy & Ceramics, College of Engineering, Mashhad Branch, Islamic Azad University,
Mashhad, Iran
Sheida Seyedi | Department of Metallurgy & Ceramics, College of Engineering, Mashhad Branch, Islamic Azad University,
Mashhad, Iran
|
|
نشانی اینترنتی |
https://jufgnsm.ut.ac.ir/article_81962_cbfbec17abc129e24a3e62735f663a11.pdf |
فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
کد مقاله (doi) |
|
زبان مقاله منتشر شده |
en |
موضوعات مقاله منتشر شده |
|
نوع مقاله منتشر شده |
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|