عنوان انگلیسی The Effect of Nickel Increasing and Aluminum Addition on Sulfidation Resistance of Fe-Ni-Cr Alloys (TECHNICAL NOTE)
چکیده انگلیسی مقاله In this research the effects of; increasing the amount of nickel and adding aluminum to create and prolong sulfidation resistance of Fe-Ni-Cr alloys have been investigated. Sulfidation tests were carried out at 1100°C in S/O bearing atmosphere. Prior to the tests, the specimens were annealed in argon at 1250°C for 8 hrs. Weight changes were measured and corroded deposits were analyzed byscanning electron microscope, X-ray diffraction, energy dispersive spectrometry and optical microscope. The results showed that, sulfidation resistance decreases as nickel content increase.Aluminum addition has good sulfidation resistance effect for these alloys, since alumina layer is more protective than chromia.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله M. Bozorgmehr |
Materials Engineering, Shahid Bahonar University of Kerman

E. Kordzadeh |
Engineering department, Iran Itok company

نشانی اینترنتی http://www.ije.ir/article_71707_edb09add401a41b3cb5c79f7f0ecefd6.pdf
فایل مقاله اشکال در دسترسی به فایل - ./files/site1/rds_journals/409/article-409-2422165.pdf
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات