علوم و تکنولوژی پلیمر، جلد ۲۱، شماره ۲، صفحات ۱۰۷-۱۱۷
|
|
|
| عنوان فارسی |
بررسی چقرمگی شکست مواد پلیمری ترد در بارگذاری مرکب کششی- برشی |
|
| چکیده فارسی مقاله |
|
|
| کلیدواژه‌های فارسی مقاله |
|
|
| عنوان انگلیسی |
Fracture Toughness Evaluation for Brittle Polymers under Combined Tensile-shear Loading |
|
| چکیده انگلیسی مقاله |
Fast fracture is one of the major failure modes in brittle polymers. Generally, crack growth in these polymers may occur under combined tensile-shear loading. However, the fracture test data reported previously for some dental restorative resins can not be predicted by using the available fracture criteria.In this paper, a modified fracture criterion is used for estimating the fracture load for the mentioned resin samples. It is shown that by considering a more accurate description for the crack tip stresses and also by accounting for the craze zone effects in front of the crack tip, the modified criterion presents significantly better predictions for the fracture resistance in such brittle polymers. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
محمدرضا محمدعلیها | mohammad reza mohammad aliha
مجیدرضا آیت الهی | majid reza
|
|
| نشانی اینترنتی |
http://jips.ippi.ac.ir/article_758_290.html |
| فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/968/article-968-197418.pdf |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
fa |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|