علوم و تکنولوژی پلیمر، جلد ۲۲، شماره ۳، صفحات ۲۲۵-۲۳۲
|
|
|
| عنوان فارسی |
تهیه و بررسی خواص فیزیکی فیلم کامپوزیتی زیست تخریب پذیر نشاسته –CMC حاوی نانوذرات مونت موریلونیت |
|
| چکیده فارسی مقاله |
|
|
| کلیدواژه‌های فارسی مقاله |
|
|
| عنوان انگلیسی |
Preparation and Study of Physical Properties of Starch-CMC Biodegradable Composite Film Containing Montmorillonite Nanoparticles |
|
| چکیده انگلیسی مقاله |
Novel citric acid modified starch-carboxy methyl cellulose (CMC) -montmorillonite (MMT) bionanocomposite films were prepared by casting method and the effect of MMT on the structural and physical properties of the starch-CMC biocomposites was studied. X-ray diffraction test showed thatstrong polar interactions between the hydroxyl groups present in the starch and CMC chains and in the silicate layers led to intercalation of biopolymer chains into MMT layers galleries. The water vapor permeability decreased from 2.44 to 1.13×10-7 g/mhPa as the MMT percentage increased from0 to 7%. At the level of 7% MMT, the composite films showed the highest ultimate tensile strength (27.55 MPa) and lowest strain-to-break (18.25%). The DSC tests showed that, the temperature position of the melting peak increased from 221.5°C to 243.0°C as MMT content increased from 1 to 7%, but the glass transition decreased and gradually disappeared. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
هادی الماسی |
بابک قنبرزاده |
علی اکبر انتظامی | ali akbar
|
|
| نشانی اینترنتی |
http://jips.ippi.ac.ir/article_698_285.html |
| فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/968/article-968-197369.pdf |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
fa |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|