علوم و تکنولوژی پلیمر، جلد ۲۳، شماره ۲، صفحات ۱۷۱-۱۷۹
|
|
|
| عنوان فارسی |
بررسی اثر شرایط فرایند ساخت محصول افزایشی منیزیم کلرید بر ساختار بلوری پایه در کاتالیزور زیگلر- ناتا |
|
| چکیده فارسی مقاله |
|
|
| کلیدواژه‌های فارسی مقاله |
|
|
| عنوان انگلیسی |
Process Conditions in Preparation of MgCl2 Adduct on Crystalline Structure of the Support in ZN Catalyst |
|
| چکیده انگلیسی مقاله |
MgCl2/C2H5OH adducts with constant relative ratio of 1/3 were prepared and kept at 120oC for different lengths of times of 5, 10, 20, 30, 50, 90,120 and 220 h. Then the samples were quenched and analyzed by XRD and BET. No meaningful changes were observed in the specific surface area of the samples, while XRD spectra showed 3 peaks at 2θ< 15o for samples kept at 120oC for 5 h. These 3 peaks were gradually replaced by a single peak for samples kept at120 oC for 120 h and beyond. Dealcoholation of the samples caused a dramatic change in specific surface area from 3.6 m2/g to 284.7 m2/g. Also XRD indicated that the peak at 2θ < 15o totally vanished and it was replaced by a weak amorphous type of peak. Catalysts produced from these supports were used to polymerize ethylene. It was observed that with increasing the specific surface area of the supports and the time of polymerization, the activity of the catalysts was enhanced dramatically. |
|
| کلیدواژه‌های انگلیسی مقاله |
support, adduct, MgCl2, ZN catalyst, polyolefin |
|
| نویسندگان مقاله |
نعیمه کلته |
مهدی نکومنش حقیقی |
پژوهشگاه پلیمر و پتروشیمی ایران
سازمان اصلی تایید شده: پژوهشگاه پلیمر و پتروشیمی ایران
حسن عربی |
|
|
| نشانی اینترنتی |
http://jips.ippi.ac.ir/article_659_278.html |
| فایل مقاله |
اشکال در دسترسی به فایل - ./files/site1/rds_journals/968/article-968-197333.pdf |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
fa |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|