عنوان انگلیسی The Effects of Nano In2O3 and ZnO on the CO Gas Detection of the SnO2 Sensor
چکیده انگلیسی مقاله The pellet-type SnO2 sensor was synthesized by the solid state method and the effects of additives such as nano ZnO (1-12 mol %) and nano In2O3 (1-10 mol %) on the CO gas sensitivity of sensor were investigated. The optimum sintering temperature was chosen 800°C because of the porosity content of the samples. The phase analysis and microstructure of the samples were studied by x-ray diffraction and scanning electron microscopy, respectively. Results show that the electrical resistivity variations of the samples with time increased by increasing the amount of additives up to the optimum value for each additive. These optimum values were 10 and 7.5mol% for nano ZnO and nano In2O3, respectively. The best sensitivity and recovery and response times were obtained in the co-doped sample containing 10 mol% nano ZnO and 7.5 mol% nano In2O3. The higher values of the additives decreased the sensitivity of the samples due to the formation of undesirable phases.
کلیدواژه‌های انگلیسی مقاله SnO2 Sensor,ZnO,In2O3,CO Gas,resistivity
نویسندگان مقاله بابک هاشمی |
department of materials science and engineering, school of engineering, shiraz university, shiraz, iran
سازمان اصلی تایید شده: دانشگاه شیراز (Shiraz university)

r atazadegaan |
department of materials science and engineering, school of engineering, shiraz university, shiraz, iran
سازمان اصلی تایید شده: دانشگاه شیراز (Shiraz university)

نشانی اینترنتی http://jufgnsm.ut.ac.ir/article_35915_188524cf7b2c7bf09ef455425a9072f6.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات