عنوان انگلیسی Characterization of Rod-like High-purity Fluorapatite Nanopowders Obtained by Sol-gel Method
چکیده انگلیسی مقاله high purity fluorapatite (FA) with rod-like and spherical-like morphology was synthesized via sol-gel method. Chemical characterization of FA powders was done by XRD and FTIR analyses. Crystallite samples were calculated using Scherer method. Morphology of FA powders was investigated with TEM and SEM images. The results revealed that increasing the time of hydrolysis of phosphate sols significantly decreased the gelation time of FA sols. Also, mixing temperature of P and Ca sols affects the gelation time of samples and increasing pH decreases the gelation time of FA sols. Morphological and chemical characterization of samples showed that the FA powders have high purity and rod-like and spherical-like morphology.
کلیدواژه‌های انگلیسی مقاله Fluorapatite,Sol-Gel,Rod-like,High-purity,Nanopowders
نویسندگان مقاله نسرین ساسانی |
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad, mashhad, iran
سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

حیدر خدیوی آیسک | khadivi ayask
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad, mashhad, iran
سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

سید مجتبی زبرجد | seyed mojtaba
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad, mashhad, iran
سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

جلیل وحدتی خاکی | vahdati khaki
department of materials science and engineering, engineering faculty, ferdowsi university of mashhad, mashhad, iran
سازمان اصلی تایید شده: دانشگاه فردوسی (Ferdowsi university)

نشانی اینترنتی http://jufgnsm.ut.ac.ir/article_35909_50606b5089daf2b19a977a5b2a778b7d.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات