عنوان انگلیسی Studies on Properties of AgAl2O3 Nanocomposite Synthesized by Solution Combustion Technique Under Novel Condition
چکیده انگلیسی مقاله AgAl2O3 nanocomposite were synthesized by solution combustion Technique using ammonium carbonate as a new fuel under simultaneous combustion of alumina and silver particles condition. Samples prepared with different amount of silver, were characterized by XRD, BET, SEM and optical Absorption measurements. XRD analysis was used to determine the change in phase and size of the synthesized nanoparticle with adding silver. BET analysis showed that added silver reduced specific surface but which is still suitable for catalytic application. BJH analysis showed that pores in Ag/Al2O3 nano composite are mesoporous and in Al2O3 nano particles is microporous. TEM and SEM showed that silver was distributed completely homogenously in pores of Alumina, and didn’t change in surface of Alumina. Optical transmission showed the different existence of different Ag species.
کلیدواژه‌های انگلیسی مقاله nanocomposite,Solution combustion,AgAl2O3
نویسندگان مقاله z ناعمی |
department of physics, university of semnan, semnan, iran.
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

m جعفر تفرشی | jafar tafreshi
department of physics, university of semnan, semnan, iran.
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

m فضلی |
department of chemistry, university of semnan, semnan, iran.
سازمان اصلی تایید شده: دانشگاه سمنان (Semnan university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5368_0dea5ea99bdb85e6272445ee8acb2af2.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات