عنوان انگلیسی Sol-Gel Synthesis, Characterization and Optical Properties of Bi 3+ - Doped CdO Sub-Micron Size Materials
چکیده انگلیسی مقاله Highly crystalline Bi3+-doped cadmium oxide (CdO) sub-micron structures were synthesized by calcination the obtained precursor from a sol-gel reaction. The reaction was carried out with cadmium nitrate (Cd(NO3)2.4H2O), bismuth nitrate (Bi(NO3)3.5H2O) and ethylene glycol (C2H6O2) reactants without any additives at 80°C for 2h. Resulting gel was calcined at 900 °C with increasing temperature rate of 15°C per minute for 12 h in a furnace. As a result of heating, the organic section of gel was removed and Bi3+-doped cadmium oxide micro structure was produced. The obtained compound from the sol-gel technique possesses a cubic crystalline structure at micro scale. Powder x-ray diffraction (PXRD) study indicated that the obtained Bi3+-doped CdO has a cubic phase. Also, SEM images showed that the resulting material is composed of particles with the average diameter of 1 µm. Also, UV–vis and FT-IR spectroscopies were employed to characterize the Bi3+-doped CdO micro structures.
کلیدواژه‌های انگلیسی مقاله Bismuth,Cadmium Oxide,Optical properties,PXRD,Sol-gel method
نویسندگان مقاله sh خادمی نیا |
department of inorganic chemistry, faculty of chemistry, university of tabriz, tabriz, iran
سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

a عالمی |
department of inorganic chemistry, faculty of chemistry, university of tabriz, tabriz, iran
سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

s وو جو | woo joo
school of mechanical engineerng wcu nano research center,yeungnam university,gyongsan 712-749 , south korea

m دولت یاری |
laboratory of nano photonics amp;amp; nano crystals, school of engineering-emerging technologies, university of tabriz, tabriz, iran
سازمان اصلی تایید شده: دانشگاه تبریز (Tabriz university)

h مرادی |
faculty of chemistry, islamic azad university, ardabil branch, ardabil, iran
سازمان اصلی تایید شده: دانشگاه آزاد اسلامی علوم و تحقیقات (Islamic azad university science and research branch)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_5441_c2840cbd17394e3fc41098e9b9801c1d.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات