عنوان انگلیسی Luminescence Properties Of Pure CaSO4 Nanoparticles Produced By Co- Precipitation Method
چکیده انگلیسی مقاله Thermoluminecsence (TL) characteristics of pure CaSO4 nanoparticles produced by co-precipitation method are presented. The formation of the nanoparticles was confirmed by X-ray diffraction (XRD) and scanning electron microscope (SEM). TL glow curve of this phosphor, exposed to gamma radiation exhibits five overlapping glow peaks in the complex glow curve at 463, 470, 483, 498 and521(K) respectively, using a computerized glow curve deconvolution procedure. A photoluminescence (PL) emission band at 393 nm was observed for the synthesized nanoparticles. Different synthesis conditions were examined in order to achieve highest TL sensitivity. The produced nanoparticles exhibit superior thermoluminescent sensitivity compared to that of its bulk equivalent.
کلیدواژه‌های انگلیسی مقاله
نویسندگان مقاله m محرابی |
institute of nano science and nano technology, university of kashan, kashan, p. o. box. 87317–51167, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

m زاهدی فر |
institute of nano science and nano technology, university of kashan, kashan, p. o. box. 87317–51167, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

e صادقی |
institute of nano science and nano technology, university of kashan, kashan, p. o. box. 87317–51167, iran
سازمان اصلی تایید شده: دانشگاه کاشان (Kashan university)

نشانی اینترنتی http://jns.kashanu.ac.ir/article_8486_8b8d7621e550130166bfeadb9ba9779f.pdf
فایل مقاله فایلی برای مقاله ذخیره نشده است
کد مقاله (doi)
زبان مقاله منتشر شده en
موضوعات مقاله منتشر شده
نوع مقاله منتشر شده
برگشت به: صفحه اول پایگاه   |   نسخه مرتبط   |   نشریه مرتبط   |   فهرست نشریات