An Investigation of Wood-Plastic Novolac Modified by Biomass Pyrolysis Oils |
|
| چکیده انگلیسی مقاله |
The possibility of using water insoluble fraction from biomass pyrolysis oil as additive in synthesis of Wood-Plastic novolac has been proved by using Differential Scanning Calorimetry (DSC) and Fourier Transformed Infra Red (FT-IR) spectroscopy. Synthesis of novolac with different concentrations (10, 20 and 30 wt %) of water insoluble fraction were performed. It was found that mechanical properties were improved by using water insoluble fraction as additive. However, furthe increasing amount of water insoluble fraction, the mechanical properties of wood-plastic novolac were decreased. When the amount of water insoluble fraction in wood-plastic novolac was 10%, the flexural strength of wood-plastic novolac was 57.8 MPa, tensile strength was 29.5 MPa. The performance and thermal behavior of novolac were characterized by DSC and TG. |
|
| کلیدواژه‌های انگلیسی مقاله |
Biomass,pyrolysis,Novolac,Preparation |
|
| نویسندگان مقاله |
xu junming |
institute of chemical industry of forest products, caf, najing 210042, china
jiang jianchun |
institute of chemical industry of forest products, caf, najing 210042, china
کانگ سون |
institute of chemical industry of forest products, caf, najing 210042, china
|
|
| نشانی اینترنتی |
http://www.ijcce.ac.ir/article_6360_6f9fa73f71f78bd853574d1524f50051.pdf |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|