Corrosion Inhibition Effect of Ester Containing Cationic Gemini Surfactants on Low Carbon Steel |
|
| چکیده انگلیسی مقاله |
α, ω-alkane-bis(N-myristoyloxyethyl-N, N-dimethyl)-diammonium bromide were synthesized and confirmed by FT-IR, FT-Raman and 1H-NMR spectroscopy. Surface tensions were measured by sigma 70 and conductivity meter EC-470C. Critical micelle concentration values were 2.70×10-4∼3.05×10-4 mol/L. The Krafft points were measured at 39.1 ~ 43.2℃. Their inhibition effects on the corrosion of low carbon steel were tested by the weight loss method in hydrochloric acid. The corrosion inhibition capacity of synthesized cationic gemini surfactant was 24.8% at 1 X 10-7mol/L concentration. Corrosion inhibition efficiency has increased by 93.8% after the concentration was increased to 1 X 10-4mol/L. As a result, these surfactants are expected to be applied as corrosion inhibitors. |
|
| کلیدواژه‌های انگلیسی مقاله |
|
|
| نویسندگان مقاله |
جنگ kwon سونگ گو | jong kwon
department of engineering chemistry, chungbuk national university cheongju 362-763, republic of korea
noh hee jeong | noh hee
department of engineering chemistry, chungbuk national university cheongju 362-763, republic of korea
|
|
| نشانی اینترنتی |
http://www.ijcce.ac.ir/article_18811_98d323656a51dbdb45090024db48cdab.pdf |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
|
| زبان مقاله منتشر شده |
en |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
|
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|